Highly polished 100mL YSZ (Yttrium stabilized ZrO2) zirconium oxide jars, 60 times the hardness of regular steel, highly wear-resistant and resistant to acid and solvents. Each jar set includes grinding jar, jar lid, rubber sealing gasket and different sizes of mixed zirconium oxide grinding balls (see detail table below).
Highly polished 100mL YSZ (Yttrium stabilized ZrO2) zirconium oxide jars, 60 times the hardness of regular steel, highly wear-resistant and resistant to acid and solvents. Each jar set includes grinding jar, jar lid, rubber sealing gasket and different sizes of mixed zirconium oxide grinding balls (see detail table below).
Composition
Bulk density
5.95 g/cm3
Zr(Hf)O2
94.48%
Y2O3
5.15%
TiO2
0.0018%
P
<0.035%
SiO2
0.007%
Fe2O3
0.0009%
S
<0.03%
N
<0.25%
L.O.I (1000C)
2.78%
Rockwell hardness
>89 HRA
Ball configurations
50ml
100ml
250ml
500ml
1000ml
Ball size/qty (pcs)
5mm
50
100
250
500
1000
10mm
8
16
50
100
200
20mm
2
3
Specifications
Jar size
50 ml
100 ml
250 ml
500 ml
1 L
Compatible ball mill
PQ-N04
PQ-N04
PQ-N2
PQ-N2, PQ-N4
PQ-N4
Outer diameter (OD)
64.9 mm
64.9 mm
89 mm
106 mm
130 mm
Inner diameter (ID)
52.85 mm
52.85 mm
73 mm
90 mm
108 mm
Total height
49.30 mm
71 mm
92 mm
105 mm
160 mm
Depth
35 mm
55 mm
75 mm
87 mm
108 mm
Total weight
1.5 lbs.
2 lbs.
3.8 lbs
5.5 lbs.
8.5 lbs.
Zirconium oxide content
> 94.2%
> 94.2%
> 94.2%
> 94.2%
> 94.2%
Rockwell hardness
> 89 HRA
> 89 HRA
> 89 HRA
> 89 HRA
> 89 HRA
Density
> 5.95 g/cm3
> 5.95 g/cm3
> 5.95 g/cm3
> 5.95 g/cm3
> 5.95 g/cm3
Max working temperature
320°C
320°C
320°C
320°C
320°C
Tolerance: +/- 2-3 mm