Highly polished 100mL YSZ (Yttrium stabilized ZrO2) zirconium oxide jars, 60 times the hardness of regular steel, highly wear-resistant and resistant to acid and solvents. Each jar set includes grinding jar, jar lid, rubber sealing gasket and different sizes of mixed zirconium oxide grinding balls (see detail table below).
Composition
Bulk density |
5.95 g/cm3 |
Zr(Hf)O2 |
94.48% |
Y2O3 | 5.15% |
TiO2 | 0.0018% |
P |
<0.035% |
SiO2 |
0.007% |
Fe2O3 |
0.0009% |
S |
<0.03% |
N |
<0.25% |
L.O.I (1000C) |
2.78% |
Rockwell hardness | >89 HRA |
Ball configurations
|
50ml |
100ml |
500ml |
1000ml |
|
Ball size/qty |
5mm |
50 |
100 |
500 |
1000 |
10mm |
8 |
16 |
100 |
200 |
|
20mm |
|
|
2 |
3 |
Specifications
Jar size | 50 ml | 100 ml |
500 ml | 1 L |
Compatible ball mill | PQ-N04 | PQ-N04 |
PQ-N2, PQ-N4 |
PQ-N4 |
Outer diameter (OD) |
64.9 mm | 68 mm | 106 mm | 130 mm |
Inner diameter (ID) | 52.85 mm | 54 mm | 90 mm | 108 mm |
Total height | 49.30 mm | 71 mm | 105 mm | 160 mm |
Depth | 35 mm | 55 mm | 87 mm | 108 mm |
Total weight | 1.5 lbs. | 2 lbs. |
5.5 lbs. |
8.5 lbs. |
Zirconium oxide content | > 94.2% | > 94.2% | > 94.2% | > 94.2% |
Rockwell hardness | > 89 HRA | > 89 HRA | > 89 HRA | > 89 HRA |
Density | > 5.95 g/cm3 | > 5.95 g/cm3 | > 5.95 g/cm3 | > 5.95 g/cm3 |
Max working temperature | 320°C | 320°C | 320°C | 320°C |
Tolerance: +/- 2-3 mm